Home - Products - Marine Line - Yachting Line - Converters & Colourants - Polyurethane texturized enamel
Polyurethane texturized enamel

Polyurethane texturized enamel

pdf-icon

Code: 4DNE00

FOR TINTING SYSTEM USE. Two component polyurethane enamel providing a semi-gloss texturized finish for application as a topcoat for boats and for industrial machineries. Thanks to its texturized finish allows to hide uneven surface or irregularities which can be present on the surface. Resistant to agressive environment.

SURFACE PREPARATION AND APPLICATION

Bare Steel. Onto sandblasted steel according to SA 2,5 apply two coats of EPOZINC 2C or EPOFOND AM-9. If sandblasting would not be possible degrease the surface and remove any trace of corrosion providing a suitable anchor pattern. Any loose paint should be meccanically removed. Apply 2 coats of EPOFOND AM-9 primer and let dry. Fill up if necessary with PLAMUR FINISHER LIGHT. Apply then one coat of POLIFOND primer, let dry for 24 hours and sandpaper. Overcoat with 2 coats of  POLYURETHANE TEXTURIZED ENAMEL allowing 18-24 hours between coats.
 
Fibreglass.
The surface to be coated should be degreased with suitable cleaner, rinsed and slightly sanded with fine abrasive paper. Remove dust and clean the surface. If the surface is slightly powdering it is necessary to apply one coat of POLIFIBER PRIMER allowing 18-24 hours between coats. Fill up if necessary with PLAMUR FINISHER LIGHT. Overcoat with 2 coats of  POLYURETHANE TEXTURIZED ENAMEL. allowing 24 hours between coats.

Bare Wood.
The surface should be clean, dry and well seasoned. If required apply a sealing coat of POLIGLASS VARNISH diluted 50% or more with THINNER 203. After 24 hours sandpaper and apply 2 coats of   POLYURETHANE TEXTURIZED ENAMEL allowing 24 hours between coats.

Previously painted wood. Proceed with a patch test on a small area of the coated surface to verify if the old paint is compatible and to make sure that the old coating is still in sound condition. If the old coating is in good conditions and of 2-pack polyurethane nature, apply then one coat of POLIFOND and let dry for 12-24 hours. Sandpaper and overcoat with 2 coats of  POLYURETHANE TEXTURIZED ENAMEL allowing 18-24 hours between coats.

In the case of loose or powdery paint or if not compatile it is recommended that the old paint should be removed completely down to bare wood and that application directions as described above for bare wood be followed.

 

Binder type A Poliurethane
Binder type B Aliphatic Isocyanate
Specific gravity kg/lt (±0,05) 1.360 (A) 1.000 (B)
Solids content (weight) ±2 70%
Solids content (volume) ±2 56%
Viscosity Ford ø 8 at 20°C ±2 Tixotropico
Shelf life +23°C (±2) 24 months in unopened cans
Application Brush-Roller
Mixing ratio A+B by weight 8 parts of Sol.A (Base+ Colourants) with 1 part Sol.B
Pot life A+B (20°C) use within 4 hours
Brush-Roller 2-5% Thinner 203 (Light textured enamel)
Spray 2-5% Thinner 203 (Light textured enamel)
Dust dry 30-40 minutes (20c)
Recoat time 24 h
Application temperature Between +10 C and +40 C
Relevant humidity Less than 80%
Dry film thickness advised 100 microns per mano
Theoret. coverage m2/Lt 3-4 m2/kg
Colour mixing by weight 75 parts of Neutral Base with 25 parts of Colourants

Colors: NEUTRO
Color code: 4DNE00

SAFETY PRECAUTIONS

Before starting paint application please carefully read all the safety precautions indicated on the label of each can or in the product safety data sheet available on request. For further information please do not hesitate to contact our technical staff.



NOTES

The above information is given to the best of our current knowledge, however, because the conditions of use of our products are beyond our control, no warranty is given or to be implied in respect of such information. Our technical staff can be contacted to study customer's specific requirements involving our products in order to enable their most effective use. Dilution rates and drying times must be considered only indicative, mainly related to a temperature of 20 ° C (68°F) and may vary according to prevailing temperature, in presence of particular weather conditions or depending on application procedures.